| Customization: | Available |
|---|---|
| Certification: | CE, ISO |
| Surface: | Smooth Side |
|
Still deciding? Get samples of US$ 0/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
tanks for aquaculture Impermeable hdpe geomembrane for shale oil gas and brine pool
High Density Polyethylene (HDPE) is the high density version of PE plastic and is harder and denser than the LDPE, but is less ductile, and lighter than water. Climax HDPE Film / Sheet / Liner / Geomembrane has proved to be a boon especially for developing countries like India by playing an important role to prevent the air and groundwater pollution. The best thing is that it can be easily moulded and welded together and the use of UV Stabilizers improves its weather resistance. High Density Polyethylene Geomembrane lives up to the expectations which are demanded in today's world of environmental engineering. Climax HDPE's prime motive is to keep the Nature clean.
1. Complete variety of specifications of width and thickness. Thickness:
2. 0.3-2.5mm/Width: 2-8m .
3. Excellent environmental stress resistant cracking performance.
4. Excellent performance of chemical erosion resistance.
5. Big scope of application temperature and long service life .
6. Applied in landfill waste site, sewage and filth treatment site, tailings depot and underground construction project
| property | Value | ||||||
| 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density G/CM3 | 0.939 | ||||||
| Tensile properties | |||||||
| Strength at yield. N/mm | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
| Break at yield.N/mm | 20 | 27 | 33 | 40 | 53 | 67 | 80 |
| Elongation at yield.% | 12 | ||||||
| Elongation at break. % | 700 | ||||||
| Right angle tear strength.N | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
| Puncture strength,N |
240 | 320 | 400 | 480 | 640 | 800 | 960 |
| Stress crack resistance using notched constant tensile loaad.H |
300 | ||||||
| Carbon Black content of a % |
2.0-3.0 | ||||||
| standard OIT,MIN:or |
100 | ||||||
| Pressure OIT,MIN | 400 | ||||||
| Baking 90d Later,Reserved standard OIT%; or | 55 | ||||||
| Baking 90d Later,Reserved Pressure OIT%; | 80 | ||||||
| Irradiate with UVA after 1600H,Reserved Standard OIT%; or |
50 | ||||||
| Irradiate with UVA after 1600H,Reserved Pressure OIT%; |
50 | ||||||
| -70ºC Embrittlement of low-temperature impact | Passed | ||||||
| coefficient of permeability of water steam G,CM/(CM2.S.PA) | ≤1.0*10-13 | ||||||
| Dimensional Stability(%) | ±2 | ||||||