| Customization: | Available |
|---|---|
| Certification: | CE, ISO |
| Surface: | Smooth |
|
Still deciding? Get samples of US$ 50/Square Meter
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
NO |
Item |
Value | ||||||
| 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| 1 | Density (g/cm2) | 0.939 | ||||||
| 2 | Tensile propeties | |||||||
| Yield strength (N/mm) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Break strength (N/mm) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yield elongation (%) | 12 | |||||||
| Break elongation (%) | ≥450 | |||||||
| 3 | Tear resistance (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
| 4 | Puncture resistance (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
| 5 | Stree crack tensistance (h) | ≥1500 | ||||||
| 6 | Carbon black | |||||||
| Carbon black content (%) | 2.0-3.0 | |||||||
| Carbon black dispersion | Carbon black dispersion (only near spherical agglomerates)fo r10 different | |||||||
| views 9 in categories 1 or 2 and 1 in category3 | ||||||||
| 7 | Oxidative induction time(OIT) | |||||||
| Standard OIT(min) | 100 | |||||||
| High pressure OIT(min) | 400 | |||||||
| 8 | Oven aging at 85°C | |||||||
| Standard OIT-% retained after 90 days (%) | 55 | |||||||
| High pressure OIT-% retained after 90 days (%) | 80 | |||||||
| 9 | UV Resistance | |||||||
| Standard OIT retained after 1600 hrs (%) | 50 | |||||||
| High pressure OITretained after 1600 hrs (%) | 50 | |||||||
| 10 | Low tempreture impact brittle property at -70°C | Pass | ||||||
| 11 | Premeability ( g.cm/(cm2).Pa) | ≤1.0×10-13 | ||||||
| 12 | Dimensional stability (%) | ±2 | ||||||
){kind=link}