1. Complete variety of specifications of width and thickness. Thickness:
2. 0.3-2.5mm/Width: 2-8m .
3. Excellent environmental stress resistant cracking performance.
4. Excellent performance of chemical erosion resistance.
5. Big scope of application temperature and long service life .
6. Applied in landfill waste site, sewage and filth treatment site, tailings depot and underground construction project
property | Value | ||||||
0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
Density G/CM3 | 0.939 | ||||||
Tensile properties | |||||||
Strength at yield. N/mm | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
Break at yield.N/mm | 20 | 27 | 33 | 40 | 53 | 67 | 80 |
Elongation at yield.% | 12 | ||||||
Elongation at break. % | 700 | ||||||
Right angle tear strength.N | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
Puncture strength,N |
240 | 320 | 400 | 480 | 640 | 800 | 960 |
Stress crack resistance using notched constant tensile loaad.H |
300 | ||||||
Carbon Black content of a % |
2.0-3.0 | ||||||
standard OIT,MIN:or |
100 | ||||||
Pressure OIT,MIN | 400 | ||||||
Baking 90d Later,Reserved standard OIT%; or | 55 | ||||||
Baking 90d Later,Reserved Pressure OIT%; | 80 | ||||||
Irradiate with UVA after 1600H,Reserved Standard OIT%; or |
50 | ||||||
Irradiate with UVA after 1600H,Reserved Pressure OIT%; |
50 | ||||||
-70ºC Embrittlement of low-temperature impact | Passed | ||||||
coefficient of permeability of water steam G,CM/(CM2.S.PA) | ≤1.0*10-13 | ||||||
Dimensional Stability(%) | ±2 |