| Customization: | Available |
|---|---|
| Certification: | CE, ISO |
| Surface: | Smooth Side |
|
Still deciding? Get samples of US$ 0/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
1. Complete variety of specifications of width and thickness. Thickness:
2. 0.3-2.5mm/Width: 2-8m .
3. Excellent environmental stress resistant cracking performance.
4. Excellent performance of chemical erosion resistance.
5. Big scope of application temperature and long service life .
6. Applied in landfill waste site, sewage and filth treatment site, tailings depot and underground construction project
| property | Value | ||||||
| 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density G/CM3 | 0.939 | ||||||
| Tensile properties | |||||||
| Strength at yield. N/mm | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
| Break at yield.N/mm | 20 | 27 | 33 | 40 | 53 | 67 | 80 |
| Elongation at yield.% | 12 | ||||||
| Elongation at break. % | 700 | ||||||
| Right angle tear strength.N | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
| Puncture strength,N |
240 | 320 | 400 | 480 | 640 | 800 | 960 |
| Stress crack resistance using notched constant tensile loaad.H |
300 | ||||||
| Carbon Black content of a % |
2.0-3.0 | ||||||
| standard OIT,MIN:or |
100 | ||||||
| Pressure OIT,MIN | 400 | ||||||
| Baking 90d Later,Reserved standard OIT%; or | 55 | ||||||
| Baking 90d Later,Reserved Pressure OIT%; | 80 | ||||||
| Irradiate with UVA after 1600H,Reserved Standard OIT%; or |
50 | ||||||
| Irradiate with UVA after 1600H,Reserved Pressure OIT%; |
50 | ||||||
| -70ºC Embrittlement of low-temperature impact | Passed | ||||||
| coefficient of permeability of water steam G,CM/(CM2.S.PA) | ≤1.0*10-13 | ||||||
| Dimensional Stability(%) | ±2 | ||||||
){kind=link}